Factory directly Uv Layer Polycarbonate Double Wall Hollow Panels - Solid&Embossed polycarbonate shet – BOFAN
Factory directly Uv Layer Polycarbonate Double Wall Hollow Panels - Solid&Embossed polycarbonate shet – BOFAN Detail:
Solid &Embossed polycarbonate sheet, Solid polycarbonate sheet, PC Solid sheets, Polycarbonate sheets, PC sheets, Embossed sheet
Products: Solid &Embossed polycarbonate sheet
Thickness: 0.8-12mm for solid PC sheet, 2-5mm for embossed PC sheet.
Width: Within 2100mm
Length: According to requests
Color: Different colors available (Clear, Brown, Blue, Green, Grey, Red, Yellow, Silver, etc)
Usage:
Swimming pool roof, Bus stop roof, Skylite, Green house, etc,
Features：
1) Light weight
2) High impact strength
3) Fire retardant
4) Good Light transmission
5) With UV protection and thermal insulation
6) Excellent physical, mechanical, and electrical properties
7) Inhibits condensation
8) Customized dimensions, thickness and colors available upon request.
| ITEM | PICTURE |
| Solid PC sheetThickness: 0.8-12mmMax. width: 1220mm |  |
| Embossed PC sheetThickness: 2.0-5mmMax.width:2100mm |  |
Technical data:
| Performance | Test Method | Units | Indicators |
| Physics | |||
| Density | g/cm3 | 1.20 | |
| Absorption,24hours | ISO 62 | mg | 10 |
| Water absorption, saturation/23℃ | ISO 62 | % | 0.35 |
| Haze astm | JG/T116-200X | % | 0.53 |
| Optical Properties | |||
| Transmittance (6mm transparent) | JG/T 116-200X | % | 88 |
| MECHANICAL Properties | |||
| Tensile yield stress- lateral | JG/T 116-200X | MPa | 66 |
| Tensile yield stress-Longitudinal | JG/T 116-200X | MPa | 66 |
| Nominal stress fracture- lateral | JG/T 116-200X | % | 95 |
| Nominal stress fracture-Vertical | JG/T 116-200X | % | 101 |
| Tensile modulus-Transverse | JG/T 116-200X | GPa | 2.4 |
| Tensile modulus-Longitudinal | JG/T 116-200X | GPa | 2.4 |
| Heating rate of change of size-horzontal | JG/T 116-200X | % | 0.3 |
| Heating rate of change of size-Vertical | JG/T 116-200X | -1.55 | |
| Yield point flexural strength, 2mm/min | ISO 178 | MPa | 90 |
| Bending Modulus, 2mm/min | ISO 178 | MPa | 2300 |
| Impact Performance | |||
| Charpy notched impact strength-level(normal termperture) | JG/T 116-200X | KJ/m2 | 11.0 |
| Charpy notched impact strength-vertical(normal termperture) | JG/T 116-200X | KJ/m2 | 11.1 |
| Perforation Features | |||
| Maximum penetration | JG/T 116-200X | 1022 | |
| Maximum penetration OF energy | JG/T 116-200X | 18.4 | |
| Hermal performance | |||
| Vicat softening temperature, B/120 | JG/T 116-200X | ℃ | 150 |
| Heat distortion temperature, 1.8 MPa | JG/T 116-200X | ℃ | 141 |
| Thermal conductitity | ISO 8302 | W/m ℃ | 0.2 |
| Coefficient of thermal expansion, 23-80℃ | ISO 11359-2 | 1/℃ | 7.00E-05 |
| Flammability | |||
| Oxygen Index | ISO 4589 | % | 25 |
| Flame Level | GB86240-1997 | B1 |
Product detail pictures:
Related Product Guide:
United Airlines ceiling panel falls after landing at Dulles International Airport (VIDEO) | Ceiling Wall Panels
Showbiz raising walls of Edmond facility this week | News | Ceiling Wall Panels
With responsible good quality method, good status and excellent client services, the series of solutions produced by our company are exported to lots of countries and regions for Factory directly Uv Layer Polycarbonate Double Wall Hollow Panels - Solid&Embossed polycarbonate shet – BOFAN, The product will supply to all over the world, such as: Latvia, Jersey, USA, By continuous innovation, we will provide you with more valuable products and services, and also make a contribution for the development of the automobile industry at home and abroad. Both domestic and foreign merchants are strongly welcomed to join us to grow together.
By June from Sri Lanka - 2016.11.11 11:41
The sales person is professional and responsible, warm and polite, we had a pleasant conversation and no language barriers on communication.
By Maria from Chile - 2015.09.23 17:37